JOURNAL OF MATERIALS CHEMISTRY
卷 21, 期 24, 页码 8854-8861出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c1jm10960j
关键词
-
资金
- EPSRC
A-site substituted cerium metavanadates, Ce1-xCaxVO3, were synthesised by solid-state reactions from single-phase powders of the corresponding orthovanadates. All metavanadate samples were found to exhibit either an orthorhombic and/or monoclinic phase of space group Pnma (62) with a = 5.5067 (4), b = 7.7904 (5) and c = 5.4814(7) angstrom for Ce0.8Ca0.2VO3. X-Ray diffraction patterns and thermal analyses have shown that the reduction of Ca-doped CeVO3 from the equivalent orthovanadate is redox phase reversible without formation of parasitic phases at x = 0.2, 0.3. Conductivity measurements were performed in air and in dry 5% H-2-Ar with conductivity of Ce1-xCaxVO3 ranging from 1.5 to 13 S cm(-1) at 700 degrees C in a reducing atmosphere. Sample Ce0.7Ca0.3VO3 exhibits the highest conductivity in a reducing atmosphere in all the measured samples which could be a potential anode or as a part of composite anode for SOFCs. The conductivity of Ce0.7Ca0.3VO3 is higher than that for Ce0.85Sr0.15VO3 which could be related to the higher doping level.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据