JOURNAL OF MATERIALS CHEMISTRY
卷 20, 期 12, 页码 2329-2335出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/b922804g
关键词
-
资金
- Royal Thai Government
Dialkyldiselenophosphinatocobalt(II), [Co(Se2PR2)(2)] (R = Pr-i, Ph and Bu-t), complexes were used to grow cobalt selenide and cobalt phosphide nanoparticles by decomposition in trioctylphosphine oxide (TOPO) or hexadecylamine (HDA) at 300 degrees C. Orthorhombic CoSe2 nanoparticles are readily formed in HDA or TOPO, whereas, in TOP/TOPO or TOP/HDA only orthorhombic CoP or Co2P nanoparticles were formed. This observation suggests that TOP provides the phosphorus for nanoparticles. The composition of cobalt phosphide can be controlled by the reaction time. Co2P was obtained after 60 min of thermolysis at 300 degrees C whereas CoP was grown over 150 min. In order to confirm the effect of TOP on the thermolysis of the precursor, the related sulfur containing precursor, [Co((S2PBu2)-Bu-t)(2)], was decomposed in TOP/TOPO, TOP/HDA, TOPO or HDA. The thermolysis reaction in TOPO or HDA gave cubic Co9S8 nanoparticles whereas in TOP/TOPO or TOP/HDA only CoP nanoparticles were formed as expected due to the presence of TOP. Characterization of these nanoparticles by transmission electron microscopy, X-ray diffraction, and electron diffraction shows highly crystalline spherical CoP and Co2P nanoparticles with a size of 5 nm diameter, and CoSe2 nanoparticles are close to cubes of ca. 10 nm size. Co9S8 nanoparticles are aggregates composed of numerous small cuboid Co9S8 nanoparticles with average diameters of 10-20 nm. The optical spectra show that Co2P and CoP nanoparticles have a band gaps (E-g) 3.14 and 1.71 eV, respectively, whilst CoSe2 nanoparticles a band gap of 1.45 eV.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据