期刊
JOURNAL OF MATERIALS CHEMISTRY
卷 18, 期 7, 页码 786-791出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/b714865h
关键词
-
This study deals with the properties of a new molecular architecture for organic thin film transistors obtained by introducing 10-decylanthr-9-yl-ethynyl moieties at the anthracene 9,10 positions. The resulting structure, formally a ter-anthrylene-ethynylene (D3ANT), is stable and endowed with sufficient solubility to guarantee the formation of good quality films. The molecule was characterised by H-1 NMR, mass spectrometry, IR, UV-vis and photoluminescence both in solution and in the solid state. Cyclic voltammetry measurements, combined with solution UV-vis, permitted the evaluation of HOMO and LUMO energy levels. A series of D3ANT-based OTFT devices were built both in bottom and top contact configurations by a spin coating technique. Top contact OTFT devices exhibited the best semiconducting characteristics, showing an average mobility of 1.2 x 10(-2) cm(2) V-1 s(-1) with on-off ratios higher then 10(4), while the highest mobility obtained was 0.055 cm(2) V-1 s(-1). AFM thin-film characterization showed evidence of a granular structure. High-resolution STM images of D3ANT monolayers adsorbed on Au(111) and HOPG reveal highly-ordered self-organized domains with molecules lying flat on the substrates, but, remarkably, no reflections were recorded by out-of plane GIXRD of spin coated films on SiO2.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据