JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 354, 期 -, 页码 231-234出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2013.11.027
关键词
Double-perovskite film; Electrophoresis technique; Crystal structure; Magnetic property
资金
- Research Project of Higher Education of Shandong Province [J11LA54]
Double perovskite Sr2FeMoO6 film was fabricated by electrophoresis method on single crystal Si substrate. The post-annealing treatment was carried out at 900 degrees C, 960 degrees C, 1060 degrees C and 1100 degrees C with 5% H-2/Ar atmosphere. Surface micrograph, structural and magnetic properties of the film have been investigated. It is found that the annealing temperature plays an important role on the phase formation and magnetic properties. According to X-ray diffraction (XRD), single phase Sr2FeMoO6 film was obtained at annealing temperature 1100 degrees C, the film shows typical polycrystal property. However, the superstructure reflection assigning the ordering arrangement of Fe and Mo atoms in the perovskite structure disappears in our XRD pattern. Raman detection finds two peaks at around 440 cm(-1) and 620 cm(-1), which belongs to Sr2FeMoO6 phase. Consistent with XRD results, typical impurity like SrMoO4 appears at around 880 cm in the film annealed at lower temperature. Microstructure investigation shows that the surface of the film is homogeneous and the grain size of particles increases with annealing temperature. Temperature dependence of magnetization reveal that the highest Curie temperature (T-C = 282 K) is obtained from the film annealed at 1100 degrees C. Owing to the large amount of anti-site defect, the highest T-C is still lower than that of parent Sr2FeMoO6 powder. (C) 2013 Elsevier B.V. All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据