JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 345, 期 -, 页码 18-23出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2013.05.030
关键词
Cobalt ferrite; Rare earth element; Heat generation application
Cobalt ferrite nano-particles, Co0.9RE0.1Fe2O4, with three different rare earth ions (Nd, Eu, and Gd) were prepared by the chemical co-precipitation method. X-ray diffraction (XRD) analysis, transmission electron microscopy (TEM), Fourier Transform Infrared (FTIR), and Vibrating Sample Magnetometry were carried out to study the structural and magnetic properties, respectively. The XRD results revealed that the crystal size is about 22 nm for Gd-Co ferrite, which is close to the particle sizes observed from TEM images (20 nm). The FTIR measurements between 350 and 4000 cm(-1) confirmed the intrinsic cation vibrations of the spinel structure. The results showed that the RE ions increase both vibrational frequencies and bond strength. The magnetic results showed that the highest magnetic coercivity and the loop area correspond to the Gd-Co ferrite, making it suitable for hyperthermia treatment. Also, the Curie point was decreased by the RE ions and had its lowest value for Nd-Co ferrite (336 degrees C). (c) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据