期刊
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 324, 期 17, 页码 2602-2608出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2012.02.106
关键词
Hexaferrite; doped hedxaferrite; Sr-Hexaferrite; Al doped Sr-Ferrite; High Coercivity Ferrite
资金
- NSF EAGER [0965801]
- Division Of Materials Research
- Direct For Mathematical & Physical Scien [0965801] Funding Source: National Science Foundation
Highly Al3+ ion doped nanocrystalline SrFe12-xAlxO19 (0 <= x <= 12), were prepared by the auto-combustion method and heat treated in air at 1100 degrees C for 12 h. The phase identification of the powders performed using x-ray diffraction show presence of high-purity hexaferrite phase and absence of any secondary phases. With Al3+ doping, the lattice parameters decrease due to smaller Al3+ ion replacing Fe3+ ions. Morphological analysis performed using transmission electron microscope show growth of needle shaped ferrites with high aspect ratio at Al3+ ion content exceeding x >= 2. Al3+ substitution modifies saturation magnetization (M-S) and coercivity (H-C). The room temperature M-S values continuously reduced while Tic value increased to a maximum value of 18,100 Oe at x=4, which is an unprecedented increase (similar to 321%) in the coercivity as compared to pure Sr-Ferrite. However, at higher Al3+ content x > 4, a decline in magnetization and coercivity has been observed. The magnetic results indicate that the best results for applications of this ferrite will be obtained with an iron deficiency in the stoichiometric formulation. Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据