Coercivity enhancement of HDDR-processed Nd-Fe-B permanent magnet with the rapid hot-press consolidation process

High coercivity, fully dense anisotropic permanent magnets of submicron grain sizes were produced by rapid hot-press consolidation of hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-Co-B powders. In the hot-press process, the coercivity of the consolidated material showed a sharp minimum prior to full densification. Thereafter, it reached a value 25% higher than that of the initial powder. Scanning electron microscopy and transmission electron microscopy observations revealed that the variation in H-cJ was caused by are distribution of Nd along the grain boundaries during hot pressing and that the high coercivity was attributable to the formation of thin, continuous Nd-rich phase along the grain boundaries. (C) 2010 Elsevier B.V. All rights reserved.