JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 323, 期 23, 页码 3104-3108出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2011.06.065
关键词
Li0.5Fe2.5O4; Particle size; Sintering temperature; Magnetization; Blocking temperature
Sintering temperature and particle size dependent structural and magnetic properties of lithium ferrite (Li0.5Fe2.5O4) were synthesized and sintered at four different temperatures ranging from 875 to 1475 K in the step of 200 K. The sample sintered at 875 K was also treated for four different sintering times ranging from 4 to 16 h. Samples sintered at 1475 K have the cubic spinel structure with a small amount of alpha-Fe2O3 (hematite) and gamma-Fe2O3 (maghemite). The samples sintered at <= 1275 K do not show hematite and maghemite phases and the crystals form the single phase spinel structure with the cation ordering on octahedral sites. Particle size of lithium ferrite is in the range of 13-45 nm, and is depend on the sintering temperature and sintering time. The saturation magnetization increased from 45 to 76 emu/g and coercivity decreases from 151 to 139 Oe with an increase in particle size. Magnetization temperature curve recorded in ZFC and FC modes in an external magnetic field of 100 Oe. Typical blocking effects are observed below about 244 K. The dielectric constant increases with an increase in sintering temperature and particle size. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据