JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
卷 21, 期 11, 页码 1042-1048出版社
SPRINGER
DOI: 10.1016/S1006-706X(14)60181-3
关键词
GCr15 SiMn; strain hardening exponent; dynamic recrystallization; critical strain; kinetic model
资金
- National High-tech Research and Development Program (863 Program) of China [2012AA03A503]
The hot deformation behavior of GCr15SiMn steel was studied through high temperature compression tests on the Gleeble-1500 thermal-mechanical simulator. The initiation and evolution of dynamic recrystallization (DRX) were investigated with microstructural analysis and then the process variables were derived,from flow curves. In the present deformation conditions, the curves of strain hardening exponent (n) and the true strain (epsilon) at the deformation temperature of 1423 K and strain rates of 0. 1, 1 and 10 s(-1) exhibit single peak and single valley. According to Zener-Hollomon and Ludwik equation, the experimental data have been regressed by using linear method. An expression of Z parameter and hot deformation equation of the tested steel were established. Moreover, the Q values of Ger15SiMn and GCr15 steels were compared. In order to determine the recrystallization fraction under different conditions, the volume fraction of DRX as a function of process variables, such as strain rate (epsilon), temperature (T), and strain (epsilon), was established. It was found that the calculated results agreed with the microstructure of the steel at any deformation conditions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据