期刊
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
卷 18, 期 11, 页码 60-66出版社
JOURNAL IRON STEEL RESEARCH EDITORIAL BOARD
DOI: 10.1016/S1006-706X(11)60118-0
关键词
super martensitic stainless steel; quenching; tempering; structure; property; reversed austenite
The microstructures and mechanical properties of Cr13 super martensitic stainless steel after different heat treatments were studied. The results show that the structures of the steel after quenching are of lath martensite mixed with a small amount of retained austenite. With the raising quenching temperature, the original austenite grain size increases and the lath martensite gradually becomes thicker. The structures of the tempered steel are mixtures of tempered martensite and reversed austenite dispersed in the martensite matrix. The amount of reversed austenite is from 7. 54% to 22. 49%. After different heat treatments, the tensile strength. the elongation and the HRC hardness of the steel are in the range of 813-1 070 MPa, 10. 1%-21. 2% and 21. 33-32. 37, respectively. The steel displays the best comprehensive mechanical properties after the sample is quenched at 1 050 C followed by tempering at 650 degrees C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据