MOD; Gd substitution; Zr dopping; YBCO film
资金
- National Basic Research Program 973 of China [2006CB601005]
- National High Technology Research and Development Program 863 of China [2009AA032401]
- National Natural Science Foundation of China [50771003]
YBCO films doped with Zr or substituted by Gd element were prepared by fluorine-reduced metal organic deposition (MOD) on LAO single crystal. The influences of different dopants on in-field critical current density (J(c)) of YBCO films were investigated. It is found that the J(c) values of YBCO films in high field were enhanced drastically through substituting Y site by Gd element partially, while the J(c) values of YBCO films in low field are not enhanced. The J(c) values of YBCO films in low field are improved significantly by adding extra Gd element into YBCO film because of the formation of rare earth oxide particles in YBCO film. But in high field, it has slight effect on J(c) values. It is an effective method to improve the property of YBCO film by adding Zr-contained compounds into YBCO film to form BZO nano particles, which cart enhance J(c) values of YBCO film in low field and M high field. Finally, the high performance Y0.5Gd0.5BCO film incorporated with BZO nano particles was prepared. The max pinning force (F-p(max)) is up to 16GN/cm(3), as higher as 4 times of that of pure YBCO film. J(c) values of Y0.5Gd0.5BCO+Zr film at 65K reach 1.31MA/cm(2)(3T) and 87.71(A/cm(2)(7T).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据