JOURNAL OF INORGANIC AND ORGANOMETALLIC POLYMERS AND MATERIALS
卷 21, 期 3, 页码 634-639出版社
SPRINGER
DOI: 10.1007/s10904-011-9500-z
关键词
Titania immobilization; Microporous perlite; Perlite granules; Millennium Degussa P25; Surface modification
资金
- University of Isfahan
Titania colloidal nanoparticles have been successfully fabricated by a very simple and inexpensive sol-gel spin-coating method on the surface perlite granules. This was achieved by adjustment of the sol-gel parameters such as the precursors, spin-coating time and heating processes. Five samples were prepared using different titania e.g. Millennium, Degussa P25, titania nanoparticle, sol-gel derived titania and rutile nanoparticles precursors. Titania nanoparticles were grown on perlite granules by the controlled immobilization of titania. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) were employed to investigate the growth and morphology of the titania coating on perlite granules. The results showed surface modification of perlite granules with uniform coating of titania on supports and confirmed that the coatings are composed of aggregated crystallites of 11-61 nm in diameter, good compositional uniformity and good adherence of the fabricated titania layer on perlite granules. The synthesis of adsorptive supports for immobilization of powdery photocatalysts would show significant improvements in both practical use and degradation efficiency of photocatalysis in environmental protection.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据