期刊
APPLIED CATALYSIS B-ENVIRONMENTAL
卷 174, 期 -, 页码 185-192出版社
ELSEVIER
DOI: 10.1016/j.apcatb.2015.03.008
关键词
Ceria; Silver; Fibrous catalyst; Diesel soot oxidation; Electrospinning
资金
- JSPS KAKENHI [26630413]
- Grants-in-Aid for Scientific Research [26630413] Funding Source: KAKEN
Ceria oxide (CeO2) nanofibers with diameters of 241-253 nm were produced via the electrospinning method. They were then applied as new support materials for silver nanoparticles and their effectiveness as diesel soot oxidation catalysts was examined. The crystal structure of the Ag was confirmed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), high-resolution transmission electron microscopy (HR-TEM), and energy dispersive spectroscopy (EDS). The diesel soot oxidation experiment was performed using a mixture of carbon black and the fabricated catalyst. In the tight contact and loose contact modes, the highest temperatures of both the CeO2-fiber-supported Ag catalysts (Ag/CeO2) calcined at 500 degrees C and the CeO2 fibers calcined at 500 degrees C were shifted to a lower temperature range, compared with JRC-CEO-3 (a commercial catalyst). In addition, the activation energy also showed similar behavior. Thus, the fibrous CeO2 and Ag/CeO2 have been shown to be effective and promising catalysts for soot oxidation. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据