期刊
JOURNAL OF ELECTRONIC MATERIALS
卷 41, 期 4, 页码 651-655出版社
SPRINGER
DOI: 10.1007/s11664-012-1934-8
关键词
Sol-gel-based electrospinning; ferroelectric nanofibers; Curie temperature; piezoelectric coefficient
资金
- National Natural Science Foundation of China (NSFC) [11032010]
- NSFC [51072171]
- PCSIRT [IRT1080]
- Natural Science Foundation of Hunan Province for Innovation Group [09JJ7004]
- Hunan Provincial Innovation Foundation for Postgraduate [CX2011B248]
- Doctoral Program of Higher Education of China [20104301110001]
Cerium-substituted bismuth titanate (BCT) nanofibers were synthesized using sol-gel-based electrospinning. The morphology, crystallized phase, and crystal structure of the nanofibers were characterized by scanning electron microscopy, x-ray diffraction, and transmission electron microscopy, respectively. Fine-crystallinity nanofibers with diameters in the range of 100 nm to 200 nm and length over 100 mu m after annealing at 750A degrees C for 1 h were obtained. The phase transition of the BCT nanofibers was investigated by thermal analysis, and the Curie temperature was found to be 540A degrees C. A displacement-voltage butterfly curve with displacement maximum of 1.1 nm was observed by piezoresponse force microscopy, and the maximum value of the piezoelectric coefficient was up to 158 pm/V, being attributed to successful Ce co-substitution for both A- and B-sites based on Raman spectrum analysis.