Thermoelectric Properties of SnO2 Ceramics Doped with Sb and Zn

Polycrystalline SnO2-based samples (Sn0.97-x Sb0.03Zn (x) O-2, x = 0, 0.01, 0.03) were prepared by solid-state reactions. The thermoelectric properties of SnO2 doped with Sb and Zn were investigated from 300 K to 1100 K. X-ray diffraction (XRD) analysis revealed all XRD peaks of all the samples as identical to the rutile structure, except for the x = 0.03 sample, which had a small amount of Zn2SbO4 as a secondary phase. We found that the power factor of the x = 0.03 sample was significantly improved due to the simultaneous increase in the electrical conductivity and the Seebeck coefficient. A power factor value of similar to 2 x 10(-4) W m(-1) K-2 was obtained for the x = 0.03 sample at 1060 K, 126% higher than that for the undoped sample.