期刊
JOURNAL OF CRYSTAL GROWTH
卷 318, 期 1, 页码 860-864出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jcrysgro.2010.11.042
关键词
Compositional deviation; Crystal morphology; Flux method; Lead-based materials; Perovskites
Relaxor antiferroelectric single crystals, lead lanthanum zirconate stannate titanate (PLZST), with compositions near the morphotropic phase boundary (MPB) were grown by the flux method using PbO-PbF2-B2O3 as a flux. Pale yellow single crystals, which were pseudo-cubes of 1.5-2 mm length and 1-2 mm thickness, were obtained. Their morphologies and chemical compositions were studied. Compositional deviation was found to occur during crystal growth. The fitted curve of the TO content in crystals versus that of in raw materials suggested that the chemical composition could draw near to MPB by adding a large amount of Ti4+ in the raw materials. XRD patterns revealed that the calcined powders experienced a gradual phase transition process from tetragonal to rhombohedral with increase in Ti4+ content. Tetragonal phase structures existed in the crystals. The gradual increase in Ti4+ content in the crystals on its increase in raw materials provides valuable information and good foundation for future work. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据