JOURNAL OF CRYSTAL GROWTH
卷 311, 期 10, 页码 3011-3014出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jcrysgro.2009.01.046
关键词
Growth from vapor; Single-crystal growth; Hydride vapor phase epitaxy; Nitrides; Semiconducting III-V materials
We succeeded in preparing very thick c-plane bulk gallium nitride (GaN) crystals grown by hydride vapor phase epitaxy. Growth of the bulk GaN crystals was performed on templates with 3 mu m GaN layer grown by metal organic chemical vapor deposition on (0001) sapphire substrates. Colorless freestanding bulk GaN crystals were obtained through self-separation processes. The crystal's diameter and thickness were about 52 and 5.8 mm, respectively. No surface pits were observed within an area of 46 mm diameter of the bulk GaN crystal. The dislocation density decreased with growth direction (from N-face side to Ga-face side) and ranged from 5.1 x 10(6) cm(-2) near the N-face surface to 1.2 x 10(6) cm(-2) near the Ga-face. A major impurity was Si, and other impurities (O, C, Cl, H, Fe, Ni and Cr) were near or below the detection limits by SIMS measurements. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据