期刊
JOURNAL OF COLLOID AND INTERFACE SCIENCE
卷 364, 期 1, 页码 1-9出版社
ACADEMIC PRESS INC ELSEVIER SCIENCE
DOI: 10.1016/j.jcis.2011.08.029
关键词
Carbon nanotube; Transparent conductive film; Electrical resistance; Flexible; Nano-silver
This study develops a technique for enhancing the electrical conductivity and optical transmittance of transparent double-walled carbon nanotube (DWNT) film. Silver nanoparticles were modified with a NH2(CH2)(2)SH self-assembled monolayer terminated by amino groups and subsequent surface condensation that reacted with functionalized DWNTs. Ag nanoparticles were grafted on the surface of the DWNTs. The low sheet resistance of the resulting thin conductive film on a polyethylene terephthalate (PET) substrate was due to the increased contact areas between DWNTs and work function by grafting Ag nanoparticles on the DWNT surfaces. Increasing the contact area between DWNTs and work function improved the conductivity of the DWNT-Ag thin films. The prepared DWNT-Ag thin films had a sheet resistance of 53.4 Omega/sq with 90.5% optical transmittance at a 550 nm wavelength. After treatment with HNO3 and annealing at 150 degrees C for 30 min, a lower sheet resistance of 45.8 Omega/sq and a higher transmittance of 90.4% could be attained. The value of the DC conductivity to optical conductivity (sigma(DC)/sigma(OP)) ratio is 121.3. (C) 2011 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据