卷 11, 期 3, 页码 421-430出版社
SPRINGER
DOI: 10.1007/s11998-013-9558-3
关键词
EIS; Montmorillonite; Nanocomposite; Uralkyd; Wood varnish
Three types of commercially modified montmorillonites (mMMT) have been tested as nanofillers in solventborne uralkyd coating compositions. The mMMT was introduced in the amount of 0.5 wt part into a coating system based on a soya oil fatty acid and isophorone diisocyanate (100 wt parts), applied onto a wood substrate, and oxidatively cured at room temperature for 14 days. An incorporation of organophilized montmorillonite into a coating composition significantly affects its viscosity (mMMT with a higher gallery space value increases that parameter) and slightly reduces the hardness of a dry coat. Moreover, a clay nanofiller increases glass transition temperature, abrasion resistance, elasticity, and impact resistance as well as barrier properties (measured using a conventional gravimetric method and an electrochemical impedance spectroscopic test) of a cured varnish. In the case of chemical resistance to acetone, lower blistering of modified coats was found.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据