JOURNAL OF CIVIL ENGINEERING AND MANAGEMENT
卷 15, 期 3, 页码 317-324出版社
VILNIUS GEDIMINAS TECH UNIV
DOI: 10.3846/1392-3730.2009.15.317-324
关键词
concrete; aggregate; expanded-clay aggregate; structural parameters; catalyst; exothermic temperature
The properties of the hardened concrete depend on the selected raw materials: size and amount of the particles of coarse aggregate, as well as on the ratio of other components. Particular countries use various methodologies for the selection of concrete composition to select the components of the concrete mixture. However, the properties of the concrete, selected by using any methodology for the selection of the concrete composition and hardened by following the defined conditions, must satisfy the values of certain necessary characteristics. The results of the implemented research indicate that the most optimal solution is to use the coarse aggregate of multi-fractional or discontinuous fractional composition. The optimal composition of the concrete must be selected to ensure that the binding material is not overdosed. Yet, all components must be selected in such a way, that the required properties of the final product are retained after concrete mixture hardens. When catalyst waste materials from the reactor of the catalytic cracking (15%) are used for the lightweight concrete, the density of the expanded-clay lightweight concrete investigated and compressive strength increases even for the higher water/cement ratio, more heat is dissipated during the hydration of the cement and this exothermic effect occurs several hours earlier.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据