JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS
卷 93B, 期 1, 页码 194-202出版社
WILEY
DOI: 10.1002/jbm.b.31574
关键词
glass ceramic; mechanical properties; cell proliferation; cell differentiation; cell adhesion
Three new chemical compositions based on the CaO-MgO-SiO2 system were designed first, and then three novel glass-ceramics (M1, M2, and M3) were prepared by sot-gel method. X-ray diffraction analysis confirmed that they were predominantly composed of akermanite, wollastonite, and dicalcium silicate crystalline phases. The coefficient of thermal expansion (CTE) of M2 was 10.79 x 10(-6)degrees C-1, closest to that of Ti-6Al-4V alloy, and the Young's modulus of M2 was 29.73 GPa, similar to that of the cortical bone. The bioactivity in vitro of M2 was evaluated by investigating its bonelike hydroxyapatite (HA)-formation ability in simulated body fluid (SBF), and the biocompatibility in vitro was detected by osteoblast proliferation, differentiation, and adhesion assay. The results revealed that M2 possessed bonelike carbonated hydroxyapatite (CHA)-formation ability in SBF and could significantly stimulate cell proliferation and differentiation. Furthermore, osteoblasts adhered and spread well on M2, indicating good bioactivity and biocompatibility in vitro. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 93B: 194-202, 2010
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据