JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS
卷 88B, 期 2, 页码 427-435出版社
WILEY
DOI: 10.1002/jbm.b.31124
关键词
dental/craniofacial material; dental/endosteal implant; nanomaterials/nanophase
The purpose of this study was to fabricate and characterize nanotubular structure on machined titanium (MA) and resorbable blast media (RBM) treated titanium by anodizing. The anodized MA and RBM were characterized with scanning electron microscopy, transmission electron microscopy, X-ray diffraction, energy disperse spectra, X-ray photoelectron spectra, and nano-indentation and scratch test. Highly ordered nanotubular layers of individually 100 nm in diameter and 500 nm in length approximately were formed regardless of the substrates. The nanotubular layers consisted mainly of amorphous TiO2 with trace fluorine. The nanotubular surfaces on both the substrates significantly reduced water contact angles and elastic modulus compared with those prior to anodizing. The anodizing treatment significantly increased the surface roughness of the smooth MA, but significantly decreased the surface roughness of the roughened RBM. The critical delamination forces of the nanotubular layer were not obtained due to the limitation of surface roughness. The anodized RBM consisted of a nano-micro porous graded structure, or a nanotubular amorphous fluoride containing TiO2 layer on top of micro-roughened titanium surface, which is expected to significantly improve the surface area that can be used to deliver drugs and growth factors and alleviate the interfacial elastic modulus mismatch as to enhance osseointegration when compared with conventional dental and orthopedic implant devices with smooth or acid etched surface. (c) 2008 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 88B: 427-435, 2009
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据