期刊
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A
卷 85A, 期 2, 页码 336-344出版社
WILEY-LISS
DOI: 10.1002/jbm.a.31523
关键词
tricalcium silicate; plaster; injectability; self-setting; bioactivity
In this study, a biphasic injectable bone substitute, based on tricalcium silicate (Ca3SiO5) and plaster (CaSO4 center dot 1/2H(2)O), is presented. The addition of CaSO4 center dot 1/2H(2)O could accelerate the hydration of Ca3SiO5, decrease the setting time, and improve the strength of the cement. The workable Ca3SiO5/CaSO4 center dot 1/2H(2)O pastes with a liquid to powder (L/P) ratio of 0.8-1.0 rnL g(-1) could be injected for 2-20 min (nozzle diameter 2.0 mm) and enabled initial setting times of 9-60 min. The setting process yielded cellular structures with compressive strength of 12.4-31.5 MPa after 2-28 days. The in vitro bioactivity of the paste was investigated by soaking in simulated body fluid (SBF) for 7 days. The result showed that although large amount of CaSO4 center dot 1/2H(2)O (30%) was added, the paste showed good ability to induce the formation of hydroxyapatite (HA). Furthermore, the Ca3SiO5/CaSO4 center dot 1/2H(2)O paste could degrade in Ringer's solution, and the dissolution extracts of the paste also had a stimulatory effect on L929 cell growth in certain concentration range. Our results indicated that Ca3SiO5/CaSO4 center dot 1/2H(2)O paste was bioactive and degradable, and showed excellent mechanical properties after self-setting. Therefore, it may be a potential candidate for further investigation as injectable tissue repairing substitute. (C) 2007 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据