JOURNAL OF APPLIED POLYMER SCIENCE
卷 135, 期 45, 页码 -出版社
WILEY
DOI: 10.1002/app.46635
关键词
adhesives; mechanical properties; thermal properties
资金
- Higher Education Commission of Pakistan
In this study, we evaluated the influence of stiff and flexible contents on the adhesive characteristics of polyurethane (PU). This was achieved through the optimization of macrodiol contents in the PU composition, which developed soft segments. The composition of the polymer comprises of two different macrodiols: poly(propylene glycol) and hydroxyl-terminated polybutadiene with various molecular weights. 4,4-Methylene bis(cyclohexyl isocyanate) was used to maximize the adhesion strength of the final product, which was evaluated with a texture analyzer. The hard-segment content (30%) positively affected the adhesive properties. The probe-tack showed a maximum adhesion energy of 147 J/cm(2), and the 180 degrees peel test showed a 15.67N/25mm peel force. The glass-transition temperature values obtained through differential scanning calorimetry were in good agreement with the theoretically calculated Flory temperature. The proportion of the loss tangent to the storage modulus showed an optimum value of 2.54 MPa-1. The accurate selection criteria of the macrodiol composition resulted in good PU pressure-sensitive adhesives. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46635.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据