fluorosilicone rubber (FSR); oil resistance; room temperature vulcanizing (RTV); thermal degradation; trifluoropropyl group
资金
- Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD)
Room temperature vulcanizing fluorosilicone rubbers (FSRs) were prepared from polydimethylsiloxane (PDMS), vinyl fluorosilicone-oil (VFS-oil), and precipitated silica (PDMS/VFS/SiO2). Rheological tests showed appropriate processing condition could be obtained when shear rate > 10 s(-1). Mechanical tests indicated that tensile strength and elongation at break were not much affected by VFS-oil and no decline was observed after being aged in 70 degrees C ASTM 1# oil. The -CF3 group could not only increase oil-resistance, but also decrease surface energy, which were proved by ATR-FTIR and contact angle tests. The PDMS oil immersion tests showed that the higher the content of VFS-oil, the better oil resistance can be obtained. The solvent-resistance tests indicated that the VFS-oil improved resistance to nonpolar/low-polar solvent. TGA results showed that the increasing content of VFS-oil could slightly decrease FSRs' thermal stability but increase FSRs' residual mass ratio at 790 degrees C. (C) 2013 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据