JOURNAL OF APPLIED POLYMER SCIENCE
卷 125, 期 5, 页码 3676-3681出版社
WILEY-BLACKWELL
DOI: 10.1002/app.36700
关键词
soybean adhesive; MUF; wet shear strength; viscosity; FTIR
资金
- National Natural Science Foundation of China [30972310/C040302, 31000268/C160302]
- Special Fund for Forestry Research in the Public Interest [201004006-2]
Soybean meal flour, polyethylene glycol (PEG), sodium hydroxide (NaOH), and a melamine-urea-formaldehyde (MUF) resin were used to formulate soybean meal/MUF resin adhesive. Effects of the adhesive components on the water resistance and formaldehyde emission were measured on three-ply plywood. The viscosity and solid content of the different adhesive formulations were measured. The functional groups of the cured adhesives were evaluated. The results showed that the wet shear strength of plywood bonded by soybean meal/NaOH adhesive increased by 33% to 0.61 MPa after adding NaOH into the adhesive formulation. Addition of PEG reduced the viscosity of the soybean meal/NaOH/PEG adhesive by 91% to 34,489 cP. By using the MUF resin, the solid content of the soybean meal/MUF resin adhesive was improved to 39.2%, the viscosity of the adhesive was further reduced by 37% to 21,727 cP, and the wet shear strength of plywood bonded by the adhesive was increased to 0.95 MPa, which met the interior plywood requirements (=0.7 MPa). The formaldehyde emission of plywood bonded by the soybean meal/MUF resin adhesive was obtained at 0.28 mg/L, which met the strictest requirement of the China National Standard (=0.5 mg/L). FTIR showed using the MUF resin formed more ?CH2? group in the cured adhesive. (C) 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据