JOURNAL OF APPLIED POLYMER SCIENCE
卷 123, 期 3, 页码 1690-1697出版社
WILEY
DOI: 10.1002/app.34655
关键词
composites; biodegradable films; methylcellulose; packaging materials; poly(caprolactone)
资金
- Natural Sciences and Engineering Research Council of Canada (NSERC)
- Quebec Ministry of Agriculture, Fishery and Food (MAPAQ)
- Le Fond Quebecois de Recherche sur la Nature et les Technologies (FQRNT)
- BSA
Methylcellulose (MC) films were prepared by casting from its 1% aqueous solution containing 0.5% vegetable oil, 0.25% glycerol, and 0.025% Tween (R) 80. Poly(caprolactone) (PCL) films were prepared by compression molding from its granules. Biodegradable composite films were fabricated using MC film as reinforcing agent and PCL as the matrix material by compression molding. One layer of MC film was reinforced with two layers of PCL films. The MC content in the composites was varied from 10 to 50% by weight. Mechanical, barrier, and degradation properties of PCL, MC, and composite films were evaluated. The values of puncture strength (PS), puncture deformation (PD), viscoelasticity (gamma) coefficient, and water vapor permeability (WVP) of the composites (50% MC content) were found to be 124.3 N/mm, 3.2 mm, 31%, and 2.6 g.mm/m(2).day.kPa, respectively. Oxygen transmission rate (OTR) of PCL, MC, and composites (50% MC) were found to be 175, 25, 22 cc/m(2)/d, respectively, which indicated that composite films showed significantly lower OTR than PCL films. Degradation tests of the composite films (50% MC) were performed for 6 weeks in aqueous medium (at 25 degrees C), and it was found that composites lost its mass slowly with time. After 6 weeks, mass and PS of the composites were decreased to 13.4 and 12%, respectively. Composite interface was studied by scanning electron microscopy (SEM). The MC film had good adhesion with PCL matrix during compression molding and suggested strong interface of the composite system. SEM image after 6 weeks of degradation showed some openings in the interface and revealed slow degradation of the MC films. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 123: 1690-1697, 2012
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据