JOURNAL OF APPLIED POLYMER SCIENCE
卷 120, 期 3, 页码 1510-1513出版社
WILEY
DOI: 10.1002/app.33291
关键词
fluoropolymers; ferroelectricity; conducting polymer; printed electronics; random access memory
资金
- Science and Technology Commission of Shanghai Municipality [07pj14029]
A ferroelectric device, making use of a flexible plastic, polyethylenterephtalate (PET), as a substrate was fabricated by all solution processes. PET was globally coated by a conducting polymer, poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) acid (PEDOT/PSSH), which is used as bottom electrode. The ferroelectric copolymer, poly(vinylidenefluoride-trifluoroethylene) (PVDF TrFE), thin film was deposited by spin-coating process from solution. The top electrode, polyaniline, was coated by solution process as well. The ferroelectric properties were measured on this all solution processed all polymer ferroelectric thin-film devices. A square and symmetric hysteresis loop was observed with high-polarization level at 15-V drive voltage on a all polymer device with 700 angstrom (PVDF TrFE) film. The relatively inexpensive conducting polyaniline electrode is functional well and therefore is a good candidate as electrode material for ferroelectric polymer thin-film device. The remnant polarization P-r was 8.5 mu C/cm(2) before the fatigue. The ferroelectric degradation starts after 1 x 10(3) times of switching and decreases to 4.9 mu C/cm(2) after 1 x 10(5) times of switching. The pulse polarization test shows switching take places as fast as a few micro seconds to reach 90% of the saturated polarization. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 120: 1510-1513, 2011
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据