photocrosslinking; ethylene-vinyl acetate copolymer; phosphorous-nitrogen compound NP28; halogen-free flame-retardant
资金
- National Natural Science Foundation of China [20704040]
- National Key Technology R&D Program of China [2007BAE27B01]
The photoinitiated crosslinking of halogen-free flame-retarded ethylene-vinyl acetate copolymer (EVA) by the phosphorous-nitrogen compound NP28 in the presence of photoinitiator and crosslinker and characterization of the related properties have been investigated by gel determination, heat extension test, thermogravimetric analysis (TGA), mechanical measurement, and thermal aging test. The photocrosslinking efficiency of EVA/NP28 blend and various factors affecting the crosslinking process, such as photoinitiator, crosslinker, NP28 content, and irradiation temperature, were studied in detail and optimized by comparison of gel content. The results show that the EVA/NP28 blend filled with 28.2 wt % NP28 with a thickness of 1.6 mm is homogeneously photocrosslinked to a gel content of above 80 wt % with 4.8 s UV-irradiation under optimum conditions. The data from TGA, mechanical measurement, and thermal aging test give evidence that the thermal stability and mechanical properties of photocrosslinked EVA/NP28 blend are much better than those of the unphotocrosslinked one. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 114: 562-569, 2009
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据