JOURNAL OF APPLIED POLYMER SCIENCE
卷 108, 期 4, 页码 2150-2155出版社
WILEY
DOI: 10.1002/app.27897
关键词
biofibers; biopolymers; degradation; mechanical properties; renewable resources
The ability of polylactide (PLA) to retain its mechanical properties after repeated cleanings at various pH levels, washing temperatures, and drying conditions has been studied. One of the problems with PLA is its poor resistance to hydrolysis, especially under alkaline conditions. In this study, PLA fabrics were sent through 50 cleaning cycles with different pH levels (8 or 10), washing temperatures (35 or 55 degrees C), and drying conditions (air dry at 21 degrees C/65% relative humidity or tumble dry at 50 or 70 degrees C). The retention percentages of the breaking tenacity, breaking elongation, and modulus of the PLA yarns were measured after every 10 cleaning cycles. A pH of 8 gave greater breaking tenacity, breaking elongation, and modulus retention than pH 10. Washing PLA at 35 degrees C and air drying it at 21 degrees C resulted in greater modulus retention than washing and drying at higher temperatures. Hydrolysis of the polymer was the main cause of the loss in mechanical properties. Equations were developed to predict the retention percentage of the breaking tenacity, breaking elongation, and modulus based on the pH, number of cleaning cycles, and washing and drying temperatures. Recommendations for appropriate conditions for the cleaning of PLA fabrics that result in greater mechanical property retention are given. (C) 2008 Wiley Periodicals, Inc.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据