We have fabricated, characterized, and compared ZnO nanorods/p-GaN and n-Zn0.94Ag0.06O nanorods/p-GaN light emitting diodes (LEDs). Current-voltage measurement showed an obvious rectifying behaviour of both LEDs. A reduction of the optical band gap of the Zn0.94Ag0.06O nanorods compared to pure ZnO nanorods was observed. This reduction leads to decrease the valence band offset at n-Zn0.94Ag0.06O nanorods/p-GaN interface compared to n-ZnO nanorods/p-GaN heterojunction. Consequently, this reduction leads to increase the hole injection from the GaN to the ZnO. From electroluminescence measurement, white light was observed for the n-Zn0.94Ag0.06O nanorods/p-GaN heterojunction LEDs under forward bias, while for the reverse bias, blue light was observed. While for the n-ZnO nanorods/p-GaN blue light dominated the emission in both forward and reverse biases. Further, the LEDs exhibited a high sensitivity in responding to UV illumination. The results presented here indicate that doping ZnO nanorods might pave the way to tune the light emission from n-ZnO/p-GaN LEDs. (C) 2014 AIP Publishing LLC.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据