JOURNAL OF APPLIED PHYSICS
卷 113, 期 16, 页码 -出版社
AMER INST PHYSICS
DOI: 10.1063/1.4803057
关键词
-
资金
- Key Project of National Natural Science Foundation of China (NSFC) [11032010]
- NSFC [51072171, 61274107, 61176093, 11275163]
- PCSIRT [IRT1080]
- 973 Program [2012CB326404]
- Key Project of Scientific Research Fund of Hunan Provincial Education Department [12A129]
- Doctoral Program of Higher Education of China [20104301110001]
Epitaxial thin films of La0.67Sr0.33MnO3/PbZr0.52Ti0.48O3 (LSMO/PZT) were deposited on SrTiO3 substrates with a SrRuO3 buffer layer by employing the pulsed laser deposition method. Its crystal structure, surface morphology, and polarization switching were investigated by using X-ray diffraction, scanning electron microscopy, and piezo-force microscopy measurements, respectively. Ferroelectric behavior along with a remnant polarization (2P(r)) of 62 mu C/cm(2), a saturated magnetization of similar to 76 emu/cm(3), and a magnetoelectric effect voltage coefficient alpha(ME) around 202 mV/cm Oe and 300 mV/cm Oe at 1 kHz were obtained successfully for the LSMO/PZT bilayers at room temperature. The result indicated that the coupling effects of electric and magnetic fields exist in the fabricated composite thin films. (C) 2013 AIP Publishing LLC.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据