The presence of superlattice reflections and detailed analysis of the powder neutron and x-ray diffraction data reveals that La rich BLF-PT (BFO0.50-LF0.50)(0.50)-(PT)(0.50) has a ferroelectric rhombohedral crystal structure with space group R3c at ambient condition. Impedance spectroscopy, dielectric spectroscopy is subset of impedance spectroscopy and ac conductivity measurements were performed in the temperature range 483 K <= T <= 573 K to probe the origin of large remnant polarization and frequency dependent broad transitions with large dielectric constant near T-c(FE). Results of impedance spectroscopy measurements clearly show contributions of both grain and grain boundaries throughout the frequency range (1 kHz <= f <= 10 MHz). It could be concluded that the grain boundaries are more resistive and capacitive as compared to the grains, resulting in inhomogeneity in the sample and cause broad frequency dependent dielectric transitions. The Maxwell-Wagner model fits very well up to similar to 10(5) Hz. Enhancement in dielectric constant and remnant polarization values are possibly due to space charge polarization caused by piling of charges at the interface of grain and grain boundaries. (C) 2012 American Institute of Physics. [doi:10.1063/1.3675279]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据