Perovskite solid solution ceramics with compositions of 0.9Pb(Fe0.5Nb0.5)O-3-0.1PbTiO(3), 0.6Pb(Ni1/3Nb2/3)O-3-0.4PbTiO(3), and 0.6Pb(Co1/3Nb2/3)O-3-0.4PbTiO(3) were synthesized by the traditional solid state reaction method. Ferroelectric measurements revealed that these samples have well saturated polarization-electrical field loops. Dielectric measurements showed that abnormal dielectric peaks at their Curie temperature were frequency dependent. Both characteristics indicate that these samples are relaxor type ferroelectric materials. Field cooled and zero field cooled magnetization measurements revealed that the 0.6Pb(Ni1/3Nb2/3)O-3-0.4PbTiO(3) and 0.6Pb(Co1/3Nb2/3)O-3-0.4PbTiO(3) samples are paramagnetic down to 5 K, while the 0.9Pb(Fe0.5Nb0.5)O-3-0.1PbTiO(3) sample shows an antiferromagnetic-like ordering starting from around 40 K. Furthermore, a weak ferromagnetism is observed in the 0.9Pb(Fe0.5Nb0.5)O-3-0.1PbTiO(3) sample, as evidenced by the magnetic hysteresis loop measured at 10 K. The ac susceptibility measurement of this sample showed that the peak position around 40 K is strongly dependent on frequency, indicating a glassy or relaxor type bahavior below that temperature. Therefore, relaxor type ferroelectric and magnetic 0.9Pb(Fe0.5Nb0.5)O-3-0.1PbTiO(3) is a magnetoelectric relaxor. (C) 2009 American Institute of Physics. [DOI: 10.1063/1.3055266]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据