期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 774, 期 -, 页码 210-221出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2018.09.321
关键词
Tungsten alloy; Zirconia; Vertical sintering; Compressive strength; Critical failure strain
资金
- National Key R & D Program of China [2017YFB0306000]
- National Natural Science Foundation of China [51672070]
The W-1.5 wt%ZrO2 alloys were prepared through azeotropic distillation method and then fabricated by four different processing techniques. The effect mechanisms of original solutions containing different acidity on the physical characteristics of the doped tungsten powders were analyzed. The doped tungsten powders with lower degree of particle agglomerates can be prepared under the condition of the original solution with the pH value of 2. Hot isostatic pressing process is beneficial to obtain higher microhardness and excellent wear resistance compared to conventional sintering, vertical sintering and hot swaging process. Meanwhile, the vertical sintering process can fabricate alloy with the compressive strength of 2090 MPa and the critical fracture strain of 0.35, approximately 24.4% and 45.8% higher than those of the swaged W-ZrO2 alloy, and approximately 55.3% and 98.1% higher than those of the swaged pure W, respectively. After swaging, though the swaged alloy has the highest density, the compressive strength and critical failure strain both decrease due to the growth of grain after annealing. The strengthening mechanisms of W-1.5%ZrO2 alloys prepared by different techniques were discussed. (C) 2018 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据