期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 601, 期 -, 页码 162-166出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.02.146
关键词
Cu and Gd-codoped CdO; Room-temperature ferromagnetism; Hydrogenation
Cadmium oxide codoped with Cu and Gd ions powders were synthesised by simultaneous thermal co-decomposition of a mixture of cadmium acetate dihydrate, bis(acetylacetonato)copper, and tris(acetylacetonato) gadolinium(III) complexes. The mass ratio of Cu/Cd is fixed while the Gd/Cd mass ratio varied systematically. The purpose of the present study is to prepare powders having room temperature ferro-magnetic (RT-FM) properties. Thus, an amount from each powder was annealed in hydrogen atmosphere in order to study its influence on the magnetic properties. X-ray fluorescence (XRF) and X-ray diffraction (XRD) methods confirm the purity and the formation of single nanocrystalline structure of the as-prepared powders, thus, both Cu and Gd ions were incorporated into CdO lattice forming solid solutions. Magnetic measurements reveal that all doped CdO powders gained paramagnetic (PM) properties where the susceptibility increases linearly with increasing dopant Gd content; the measured effective magnetic moment of doped Gd3+ was 7 mu(B). Furthermore, the created RT-FM is dependent on the Gd% doping level. Also, it was found that the hydrogenation of the powders slightly enhances their PM properties and strongly enhances or creates RT-FM. For hydrogenated CdO powder doped with 3.1% Gd, the coercivity (H-c), remanence (M-r), and saturation magnetization (M-s) were 283.2 Oe, 2.04 memu/g, and 6.67 memu/ g, respectively. Also, under hydrogenation, the values of Hc, Mr, and Ms were increased by similar to 145%, 476%, and 131%, respectively in comparison with as prepared. Thus it was proved, for the first time, the possibility of production of CdO with RT-FM, where magnetic characteristics can be tailored by doping and post treatment under H-2 atmosphere, thus a new potential candidate to be used as a dilute magnetic semiconductor (DMS). (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据