Lithium-ion battery; Electrode materials; Chemical synthesis; LiNi0.6Co0.2Mn0.2O2; Concentration-gradient
Spherical Ni0.6Co0.2Mn0.2(OH)(2) precursor with the concentration of Ni and Mn changed in opposite was prepared by co-precipitation. Then, well-ordered spherical LiNi0.6Co0.2Mn0.2O2 was synthesized by sintering the mixture of as-prepared precursor and LiOH center dot H2O first calcined at 550 degrees C for 4 h in air, followed at 820 degrees C for 12 h in flowing oxygen. Their structural and electrochemical properties were investigated using X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), charge-discharge test, cyclic voltammetry (C-V) method and electrochemical impedance spectroscopy (EIS) test. The concentration-gradient material had a superior electrochemical performances compared to conventional homogeneous LiNi0.6Co0.2Mn0.2O2 material, demonstrated by the results of C-V and EIS. The results of charge and discharge test demonstrated that the concentration-gradient LiNi0.6Co0.2Mn0.2O2 cathode material sintered at 820 degrees C delivered an initial discharge capacity of 174.3 mA h g(-1), at 1 C rate between 2.8 and 4.3 V and more than 93.1% of that was retained after 100 cycles. Besides, this material also exhibited excellent rate capability and high voltage cut-off and temperature performance. (C) 2014 Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据