Mechanical properties; Sintering; Microstructure; Ceramic; Ti(C,N)-based cermets
资金
- Program for New Century Excellent Talents in University [NCET-13-0357]
Various ratios of superfine WC and TaC particles were added into Ti(C7N3) matrices, and Ti(C7N3)-based composite cermets tool materials were prepared using a hot-pressed sintering technology by various processes. The effects of the superfine WC and TaC particles and sintering processes on the mechanical properties and microstructure were thoroughly investigated. The addition of superfine WC depressed the mechanical properties, but the addition of superfine WC and TaC together refined the microstructure, which optimised the mechanical properties of materials. Both a longer holding time and a higher sintering temperature facilitated the growth of (Ti, W, Ta, Mo)(C,N) grains that caused a reduction in the flexural strength and fracture toughness. A Ti(C7N3)-based cermets tool material with a 9 wt% WC and a 6 wt% TaC, which is sintered at 1400 degrees C with 30 min at 30 MPa, exhibits the best mechanical properties. This cermet material was then manufactured into cutting tools which maintained good wear resistance after 85 min of high-speed cutting stainless steel. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据