JOURNAL OF ALLOYS AND COMPOUNDS
卷 617, 期 -, 页码 491-497出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.08.018
关键词
Electrode materials; Energy storage materials; Nanostructured materials; Electrochemical impedance spectroscopy; Oxide materials
资金
- Dongguk University-Seoul
The various molar concentrations of cobalt doped manganese dioxide (Co-MnO2) nanostructures were synthesized by an hydrothermal technique for electrochemical supercapacitor application. The X-ray diffraction analysis showed that the samples were composed of multiphase of MnO2 with dominant reflections of gamma-MnO2 structure of crystallization. The morphological studies displayed the existence of MnO2 nanowires with the width of 10-20 nm and showing a good degree of crystallization. The electrochemical characterization was performed using cyclic voltammetry, galvanostatic charge/discharge test and impedance spectroscopy in 1 M Na2SO4 aqueous electrolyte. All the samples exhibit a typical ideal capacitive behavior with an increasing order of specific capacitance values with respect to the increase in the concentration of cobalt ions up to a certain limit. The specific capacitance of 415 F g(-1) was delivered by 5% Co-MnO2 sample at 0.2 A g(-1) which was nearly double that of bare MnO2 electrode of 231 F g(-1). Moreover, the Co-MnO2 electrode shows an excellent capacitance retention (97.3%) after 5000 charge and discharge cycles. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据