Silver nanoparticles; Truncated nanocubes; Hydrothermal synthesis; CTAB; Glucose reduction
资金
- National Science Council of Taiwan [NSC100-2221-E009-075-MY3]
A high-yield water-based hydrothermal synthesis was developed using silver nitrate, ammonia, glucose, and cetyltrimethylammonium bromide (CTAB) as precursors to synthesize truncated silver nanocubes with uniform sizes and in large quantities. With a fixed CTAB concentration, truncated silver nanocubes with sizes of 49.3 +/- 4.1 nm were produced when the molar ratio of glucose/silver cation was maintained at 0.1. The sample exhibited (100), (110), and (111) planes on the facets, edges, and corners, respectively. In contrast, with a slightly larger glucose/silver cation ratio of 0.35, well-defined nanocubes with sizes of 70.9 +/- 3.8 nm sizes were observed with the (100) plane on six facets. When the ratio was further increased to 1.5, excess reduction of silver cations facilitated the simultaneous formation of nanoparticles with cubic, spherical, and irregular shapes. Consistent results were obtained from transmission electron microscopy, scanning electron microscopy, X-ray diffraction, and UV-visible absorption measurements. (C) 2013 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据