JOURNAL OF ALLOYS AND COMPOUNDS
卷 584, 期 -, 页码 56-62出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2013.09.026
关键词
Metals and alloys; Microstructure; Corrosion; Solidification; Mechanical properties
资金
- NSFC [51101142, 50821001]
- New Century Excellent Talents in University of Ministry of Education of China [NCET-12-0690]
- Science Foundation for the Excellent Youth Scholars of Hebei Province [Y2012019]
- Science Supporting Project of Hebei Province [13961002D]
The aim of this study was to investigate the effects of super-high pressure solidification (2 and 4 GPa) on microstructures, nano-mechanical behaviors and corrosion properties of Mg-30 wt.% Al alloy. The lattice parameter (a) of Mg matrix is decreased and the c/a value is increased owing to the increased Al concentration in Mg matrix. In contrast to the as-cast sample or other super-high pressure samples, the Mg matrix is more homogeneous and the net-like eutectic phase becomes finer after super-high pressure solidification at 800 degrees C under 2 GPa. In addition, the area fraction of eutectic phase is reduced with increasing the exterior pressure and temperature during the solidification, whilst the Al concentration in both the Mg matrix and the eutectic phase are enhanced. The nanoindentation results indicate that both the hardness and Young's modulus are sensitive to the solidification pressure and temperature. The Tafel curves and electrochemical impedance spectroscopes results reveal the corrosion properties of the sample at 800 degrees C under 2 GPa are remarkably improved due to the formation of a compact and continuous oxide layer. (C) 2013 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据