Li addition; Mg-Li-Al-Sn-Mn alloy; Extrusion Microstructure; Mechanical property
资金
- Technology R&D Program for Energy [20112010300030]
- Ministry of Trade, Industry and Energy (MOTIE, Korea)
Effects of Li addition on microstructure and mechanical properties of as-cast and as-extruded Mg-xLi-3Al-1Sn-0.4Mn alloys were investigated. Mg-3 wt% Al-1 wt% Sn-0.4 wt% Mn alloys with different Li addition (5, 8 and 11 wt%) were cast under an SF6 and CO2 atmosphere at 700 degrees C and extruded at 200 degrees C. Li addition to Mg-3Al-1Sn-0.4Mn resulted in the formation of MgLi2Sn and MgLi2Al intermetallic compounds and random basal texture. With increasing Li addition from 5 to 8 and 11 wt%, ultimate tensile strength was decreased from 258 to 240 and 220 MPa. On the other hand, the elongation was improved remarkably from 16.0% to 15.4% and 35.1% at room temperature due to transformation from HCP to BCC crystal structure and a weaker basal texture. In the Mg-xLi-3Al-1Sn-0.4Mn alloys, MgLi2Sn and MgLi2Al intermetallic compounds played a significant role for the increase of the mechanical properties. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据