卷 548, 期 -, 页码 208-215出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2012.09.037
关键词
Iron deficient; Initial permeability; Relative quality factor; Complex permeability; Ferromagnetically ordered
资金
- Khulna University of Engineering & Technology, Bangladesh
Fe-deficient Ni-Cu-Zn ferrites with composition Ni0.28Cu0.10Zn0.62O(Fe2O3)(1-x), where x = 0.00, 0.02, 0.04, 0.06, and 0.08 were prepared by the double sintering ceramic technique. Real part of the initial permeability mu', Curie temperature T-c, imaginary part of the initial permeability mu '', relative quality factor (Q-factor) of the samples were elaborately discussed as a function of frequency and temperature with increase of Fe-deficiency during the heating and cooling cycles. The temperature dependence of the imaginary part of the complex permeability curves are very interesting to note that there is a peak value of mu '' at particular temperature which corresponds to the T-c because at this temperature the samples might be in complete spin disorder. This reflects that at T-c, a ferrimagnetically ordered state over comes KBT and becomes comparable with mu H-0 where the loss becomes maximum. Results of heating and cooling cycles were found to be very close to each other. The small difference during heating and cooling process might arise due to the thermal hysteresis which is accumulated in this work. In our study, it was noticed that the resonant frequency and T-c increases first with the increase in iron deficiency and decreases after it takes a maximum at x = 0.06. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据