In this work, the conductivity and electrochemical performance of compounds xLi(2)MnO(3)center dot(1 - x)LiMn1/3 Ni1/3Co1/3O2 (x = 0.1, 0.2, 0.3, 0.4) at temperature -10, 25, and 45 degrees C were investigated. Both conductivity and electrochemical performance are dependent on the content of Li2MnO3 (x). The compound with x = 0.3 has a highest AC conductivity of 4.36 x 10 S-6 cm(-1) at room temperature. The conductivity is 8.64 x 10 S-7 cm(-1) at -10 degrees C, one order smaller than 9.98 x 10 (-6) S cm(-1) at 45 degrees C. Furthermore, at a current density of 50 m Ag-1, the compound with composition at x = 0.3 showed an initial discharge capacity of 223.67 mA hg(-1) at room temperature, which increased to 238.08 mA hg(-1) at 45 degrees C and decreased to 114.5 mA hg(-1) when testing temperature was decreased to -10 degrees C. Increasing the conductivity is an effective way to get better electrochemical performances of this kind of compound at different temperatures. (c) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据