Near white light emission of BaY2ZnO5 doped with Dy3+ ions

期刊

JOURNAL OF ALLOYS AND COMPOUNDS
卷 517, 期 -, 页码 9-13

出版社

ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2011.11.088

关键词

Oxides; Phosphor; Near-white-light emission

资金

  1. National Science Council of the Republic of China [NSC 98-2221-E-150-065-MY2]

向作者/读者索取更多资源

Controlling activator concentrations to possess near white light emission of BaY2ZnO5 doped with Dy3+ ions was performed using high energy vibrating milled solid-state reaction. The XRD patterns show that all of the peaks can be attributed to the BaY2ZnO5 orthorhombic structure, because that the BaY2ZnO5 and BaDy2ZnO5 are isostructures with a space group of Pbnm. Under ultraviolet (355 nm) excitation, a weak group of emission peaks appear for the M-4(21/2) I-4(13/2) + K-4(17/2) + F-4(7/2) -> H-6(13/2) transition at 453 nm, and two groups of strong emission peaks appear at 489 nm and 579 nm, corresponding to the F-4(9/2) -> H-6(15/2) and F-4(9/2) -> H-6(13/2) transitions of Dy3+ ions, respectively. The decay curve results indicate that the decay mechanism of the F-4(9/2) -> H-6(13/2) transition is a single decay component between Dy3+ ions only. In addition, the asymmetry ratio, which is independent of Dy3+ ion concentration, remains at about 1.04, indicating that the symmetry of Dy3+ ions does not change with concentration. Concentration quenching occurs with x values above 0.07, and the critical distance is about 11.93 angstrom. The CIE color coordinates of x = 0.320 and y = 0.389 are located in the near white light region. (C) 2011 Elsevier B. V. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据