JOURNAL OF ALLOYS AND COMPOUNDS
卷 528, 期 -, 页码 40-44出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2012.03.023
关键词
Magnesium alloy; Rolling; Mechanical properties; Homogenization; Long-period stacking ordered (LPSO) phase
资金
- International Cooperation Key Project
- Ministry of Science and Technology (MOST), China [2010DFB50210]
- Project of Scientific Researchers Serving for Enterprises
- Ministry of Science and Technology, China [2009GJB20003]
In this research, the as-cast and as-homogenized Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy were subjected to the hot rolling with the same processing parameters. The microstructure and mechanical properties of the two kinds of as-rolled sheets were investigated. The sheet rolled from the as-cast alloy was mainly composed of recrystallized alpha-Mg grains surrounded by Mg-3(Gd,Y) eutectic compounds. While the sheet rolled from the as-homogenized alloy was composed of large deformed grains with long-period stacking ordered (LPSO) phase inside and fewer recrystallized alpha-Mg grains, and exhibited higher strength due to the deformed grains with stronger basal texture and larger volume fraction of long-period stacking ordered (LPSO) phase. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据