期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 509, 期 -, 页码 S770-S774出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2010.11.063
关键词
Metal hydrides; Surfaces and interfaces; Sintering; Chemical synthesis; Gas-solid reactions; Catalysis
Hydrogen storage performance of the TiFe-based materials suffers from difficulties with hydrogenation and sensitivity towards impurities in hydrogen gas reducing hydrogen uptake rates and decreasing the cycle stability. In present work the surface modification of the sintered Ti1.1Fe0.9Ox and arc-melted TiFe was performed using autocatalytic deposition of the Pd-based catalytic layers in order to achieve improvement of the H storage characteristics. Pd deposition proved to be efficient in significant facilitation of the hydrogenation ability of the materials at moderate H-2 pressures and room temperature, even after their long exposure to air. Activation performance of the sintered Ti1.1Fe0.9Ox is superior than that for the arc-melted TiFe. This effect was associated with the presence of the oxygen-containing suboxide Ti4Fe2O1-x in the sintered sample acting as a hydrogen transfer catalyst. gamma-Aminopropyltriethoxysilane pre-functionalization and subsequent Pd-P autocatalytic deposition onto the sintered Ti1.1Fe0.9Ox intermetallic substrate resulted in a better hydrogenation kinetics compared to the samples prepared by the conventional Pd deposition. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据