期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 509, 期 8, 页码 3553-3558出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2010.12.058
关键词
Glass ceramics; Eu2+/Sm3+ co-doped; SrSiO3 nano-crystals; Optical properties; White LED
资金
- National Natural Science Foundation of China [51072190, 11004177]
- Program for New Century Excellent Talents in University [NCET-07-0786]
- Zhejiang Provincial Natural Science Foundation of China [Z4100030, Y4080268]
Eu2+/Sm3+ co-doped silicate glass was prepared by high temperature melting under reducing atmosphere and the Eu2+/Sm3+ co-doped SrSiO3 transparent glass-ceramics were obtained after heat-treatment. X-ray diffraction (XRD) and Raman spectra confirmed the formation of SrSiO3 nano-crystals in the glass matrix. The photoluminescence excitation (PLE) spectra and photoluminescence (PL) spectra of the samples were measured. A broad emission band from 400 nm to 550 nm due to the 4f(6)d(1) -> 4f(7) transitions of Eu2+ was observed, as well as several sharp emission peaks at 563 nm, 600 nm, 646 nm and 713 nm ascribed to the 4f -> 4f transitions of Sm3+. The luminescence properties of the glass ceramics with different molar ratio of Eu2+/Sm3+ were studied and the corresponding chromaticity coordinates were calculated. The ultraviolet light-emitting diode (UV-LED) excitable glass-ceramics emitting white light were obtained by tuning the relative emission intensity of Eu2+ and Sm3+. The results indicate that the Eu2+/Sm3+ co-doped SrSiO3 transparent glass-ceramics can be used as a potential matrix material for White LED under UV-LED excitation. (c) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据