期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 509, 期 41, 页码 9938-9945出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2011.07.103
关键词
Metal-intermetallic composite; Accumulative roll bonding process; Mechanical properties
资金
- Shiraz University
In this research, Al/Ni multilayers composites were produced by accumulative roll bonding and then annealed at different temperatures and durations. The structure and mechanical properties of the fabricated metal intermetallic composites (MICs) were investigated. Scanning electron microscopy and X-ray diffraction analyses were used to evaluate the structure and composition of the composite. The Al3Ni intermetallic phase is formed in the Al/Ni interface of the samples annealed at 300 and 400 degrees C. When the temperature increased to 500 degrees C, the Al3Ni2 phase was formed in the composite structure and grew, while the Al3Ni and Al phases were simultaneously dissociated. At these conditions, the strength of MIC reached the highest content and was enhanced by increasing time. At 600 degrees C, the AlNi phase was formed and the mechanical properties of MIC were intensively degraded due to the formation of structural porosities. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据