Magnesium alloy; Mg-Dy-Zn alloy; Ageing behavior; Long period stacking ordered phase; Precipitation strengthening
资金
- National Nature Science Foundations of China [50771049, 50871046]
Ageing behavior of Mg-2Dy-0.5Zn alloy was investigated during isothermal ageing at 180 degrees C. Two significant ageing peaks were observed at 36 h and 80 h, respectively. Examination of microstructure evolution during ageing revealed that 14H long period stacking ordered (LPSO) phase forms in the alpha-Mg matrix and its volume fraction increases, (Mg, Zn)(x)Dy particle phases precipitate and their size, distribution and amount vary, as ageing time increases. The LPSO strengthening and the precipitation strengthening are two main mechanisms responsible for the double-peak ageing behavior observed for the Mg-2Dy-0.5Zn alloy. The first ageing peak is mainly attributed to the precipitation strengthening of a large amount of the fine (Mg, Zn)(x)Dy particle phases. The second ageing peak arises mainly from the LPSO strengthening of a high volume fraction of the 14H LPSO phase. (C) 2011 Elsevier B. V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据